优化的加工性能

At the same high loading concentration, DW-1070 causes a significantly smaller reduction in the resin's melt flow index (MFI) compared to conventional titanium dioxide of equivalent quality, thereby minimizing the impact on melt flowability. Furthermore, compounding time is shortened, and viscosity drops substantially at high shear rates, which ultimately boosts processing efficiency and finished product uniformity.

Excellent Lacing Resistance

When evaluated at an identical 70% loading across various shear rates, our product demonstrates a significantly smaller variation in viscosity compared to the benchmark titanium dioxide. This means that our product is exceptionally well-suited for high-temperature extrusion coating and lamination applications (such as packaging material production). During these high-speed, high-temperature manufacturing processes, it effectively reduces the risk of pinholes, cracking, or lacing defects on the film surface, thereby safeguarding overall product quality.

DW-1070（超分散性TiO2₂ Masterbatch) · 6575 Pa·s @ 1 s⁻¹TiO₂(616S) — Rutile reference · 20800 Pa·s @ 1 s⁻¹· 30% LDPE (12 MFI) + 70% pigment · 190 °C

图1 Melt Rheology / 70% TiO₂ vs DW-1070 in 12 MFI LDPE at 190 °C

Melt viscosity directly controls how a TiO₂-loaded compound behaves during extrusion, coating, and film-blowing. Two samples were tested at identical loading — 30% LDPE (12 MFI) as the carrier resin plus 70% of either (1) DW-1070, Super-dispersed TiO₂ Masterbatch or (2) reference rutile titanium dioxide, TiO₂(616S). At 190 °C, DW-1070 shows a much flatter viscosity profile than the reference — starting at ~6575 Pa·s vs ~20800 Pa·s at low shear, and converging at high shear. This makes DW-1070 especially suited to high-temperature extrusion coating and lamination (e.g., flexible packaging) where high speeds and high temperatures otherwise risk pinholes, cracks, and surface defects in the finished film.

提高复合效率

加入 DW-1070 可显著缩短达到均匀熔融状态所需的时间，轻松缩短加工周期。这不仅提高了生产效率，而且降低了单位能耗和总体制造成本。

DW-1070（超分散性TiO2₂ 母粒TiO₂(616S) — Rutile reference· 30% LDPE (12 MFI) + 70% pigment

图 2 内部混频器功率曲线

Internal mixer power consumption is a direct measure of how much energy is needed to incorporate and disperse a pigment into the resin. Two samples were compared in an internal mixer (Banbury / BR) — 30% LDPE (12 MFI) carrier resin plus 70% of either (1) DW-1070, Super-dispersed TiO₂ Masterbatch or (2) reference rutile titanium dioxide, TiO₂(616S). The reference powder needs full wetting and dispersive mixing — peak power climbs to ~27 kW with fusion at ~41 s. DW-1070, already pre-dispersed in carrier resin, only requires distributive blending — peak power stays around ~13 kW with fusion at ~10 s, then settles to a low, steady ~8 kW.

~52% Lower Peak Power

Pre-dispersed pigment means no need for high-energy dispersive mixing — peak motor load drops dramatically, protecting motor and gearbox from overload trips.

~4× Faster Fusion

Fusion in ~10 s instead of ~41 s shortens cycle time, multiplies batch throughput on the same equipment, and reduces residence time at high temperature.

Lower Energy & Cost per kg

Lower peak + shorter cycle = significantly less kWh per kilogram of compound, with the bonus of less wear on rotors and chamber walls.

Low Volatile Content

This prevents the formation of bubbles and silver streaks (splay marks) during processing, effectively guaranteeing a high finished product yield.

DW-1070 (PE主控)· 加热从 50°C 到 150°C

图 3 热重分析（TGA）

低挥发性成分对于高温塑料加工至关重要——过量的水分或挥发性物质会导致气泡、银纹和表面缺陷。DW-1070 即使在 150 °C 下仍能保持其初始质量的 99.5%，这证实了其超低的挥发性成分，适用于严苛的挤出和注塑成型条件。